Aluminum Die Casting

In 2011, Aluminum Die Casting  industry chain forum, Buhler’s Dr. Lu believes that the success of structural parts of the casting for the automotive industry to bring new development opportunities, die-casting industry in China should actively carry out technological development and follow-up, share casting technology advances.

 Automotive structural parts are installed on the node is the car to form the high-intensity resistance to deformation of the force bearing parts or pieces, with a large size, thin wall, the structure of complex features. In the current production methods, Structual process to adopt a common die-casting machine, with the aid of process measures and optimization of process factors, die-cast automobile part to achieve the industrial production.

 Casting automotive structural parts can be heat treatment, welding and bonding connections, quality and performance fully meet the requirements. Currently casting automotive structural parts have entered the car market in Europe, and gradually spread from the high-end cars to the middle and low range of applications continues to expand. die casting In the automotive powerhouse of China, this production method has been popularized as soon as possible.

Metal Casting

Metal mould casting production guide

This book for the metal type casting production is actual, from theory and practice system introduced in metal mold from design, production to finished product technology base knowledge, operation skills, equipment to use as well as to improve the quality of castings in the methods of content, including metal mold design, casting, metal mold design scheme, Aluminum Casting sand core / shell tribute, casting alloy, heat treatment and casting defect analysis and preventing etc.. The book proceeds the metal mould casting of Gypsies of scientific and technological achievements and commonly used standard, citing a large number of production example, facilitate the reader consults. This book is available in the field of casting technical personnel, management personnel and technical workers in enterprises in practice for reference, but also for professional colleges, research staff to read.

The progress of science and technology and our national economic development, on the casting production raised taller requirement. In recent years. Metal mold casting a wide range of applications, to further meet the needs of industrial and agricultural production, promote the development of foundry production.

At present, in the metal casting enterprises and workers is increasing day by day, I have been to many factories, and are engaged in the work of the business leaders, technical personnel and management staff to carry on the exchange, they all wanted me to write this book of practical technology, so as to guide the practice, make produce detours. Although I am in the nineteen sixties and 70’s, were prepared by the” metal mold design and manufacture”,” aluminum alloy metal casting” two books, but so long. The metal mold casting of science research and production practice, and the emergence of many new results. In order to meet the needs of the community, to further promote aluminum casting China is special casting enterprise development, I wrote the” metal type casting production guide”.

The book to sum up experiences and lessons, and the income of the latest scientific and technological achievements and Chinese and foreign relevant technical standards. In order to reflect the complete book of books, incorporated before I and Xiao Ziqiang Li Ren high school, Zhang Yanwei professor of common research and the preparation of an internal issue book in part; the book castings and tooling design, equipment design and technical parameters, most businesses to support provided by. In this heartfelt thanks to all support the book was written and published comrade.

Limited to the level, the content of the book is inappropriate, adjure a reader.

Zinc Die Casting

A group of Zinc Die Casting faucet, into the copper plating requirements for character, the polished rack to do, always do not like the color of copper, it touches like imitation gold plated color, can not be successfully repeated several times, and plating colors will fade black, is there any way to solve similar or copper color similar to black and fade after plating the problem?


The answer plating plating and die by the poor surface quality and other factors.

     Casting should ensure a good surface quality, can not have loose, cracks, holes, bubbles, shrinkage, cold pattern, defects such as pinholes, or casting surface foaming after plating, electroplating layer from the substrate.

     Grinding and polishing before plating time, careful not to grind too.

     Because die castings during solidification, due to quenching and surface form a dense layer of chilled, and the internal organization may have holes, shrinkage and other defects.

     Do not rub off this good ground surface, or when there will be pitting plating, bubbles, etc. Also, do not weight too tight hot polishing wheel, abrasives and products to prevent adhesions, resulting in poor plating products.

     Easy oxidation of zinc, Aluminum Die Casting China a long time a layer of oxide film formed on the surface, affecting performance.

     Therefore, the removal of the oxide film to have a reducing substance can be acidic (eg hydrochloric acid) solution will be in and out of the surface oxide film